Effect of hybrid reinforcement based on precipitated silica and montmorillonite nanofillers on the mechanical properties of a silicone rubber Nik I. Nik Ismail Ali Ansarifar Mo Song 2134/21473 https://repository.lboro.ac.uk/articles/journal_contribution/Effect_of_hybrid_reinforcement_based_on_precipitated_silica_and_montmorillonite_nanofillers_on_the_mechanical_properties_of_a_silicone_rubber/9234662 Silicone rubber (SR) nanocomposites containing precipitated silica (PS), montmorillonite (MMT) and PS/MMT hybrid fillers were prepared through melt-mixing technique. In the SR/PS/MMT nanocomposite, the hybrid filler weight ratio was increased progressively from 0.4 to 1.7 while keeping the MMT weight constant. The viscosity, cure characteristics and mechanical properties of the nanocomposites were subsequently measured. The optimum cure time increased and the scorch time and rate of cure decreased. Furthermore, when the hybrid filler weight ratio was raised to its optimum, the tensile strength, Young’s modulus, modulus at 100% and 300% elongation (M100 and M300), elongation at break, stored energy density at break and hardness of the nanocomposite improved. The stress-strain properties of the nanocomposite with the hybrid filler improved at high deformation in comparison with those containing the PS and MMT fillers. The MMT filler exfoliated in the SR/MMT nanocomposite but did not in the nanocomposites containing the hybrid filler. Notably, the mechanical properties of the nanocomposite benefitted from the hybrid filler. This was due to the filler-filler and filler-rubber network formation in the rubber by the PS particles. Finally, effect of the PS, MMT and hybrid fillers on the energy loss or hysteresis of the rubber was measured. 2016-06-03 14:36:48 untagged Materials Engineering not elsewhere classified