%0 Conference Paper %A Gona, Michael %A Isherwood, Patrick %A Bowers, Jake %A Walls, Michael %D 2017 %T Combinatorial study of Sn-Ti-W-O transparent conducting oxide thin films for photovoltaic applications %U https://repository.lboro.ac.uk/articles/conference_contribution/Combinatorial_study_of_Sn-Ti-W-O_transparent_conducting_oxide_thin_films_for_photovoltaic_applications/9559061 %2 https://repository.lboro.ac.uk/ndownloader/files/17191004 %K Transparent conducting oxides %K Amorphous thin films %K Magnetron reactive sputtering %K Combinatorial technique %K Mechanical Engineering not elsewhere classified %X a combinatorial study of transparent conducting oxide thin films based on SnO2–TiO2-WO3 phase space is reported. These multinary oxide films were fabricated by magnetron reactive co-sputtering of tin monoxide (SnO), titanium (Ti) and tungsten (W) targets. SnO2–TiO2-WO3 film compositions with Ti/Sn ratio (0.02 – 0.12) and W/(Ti+Sn) ratio (0.02 – 0.25) were explored. The effect of oxygen partial pressure on composition, structure and optical properties was evaluated. High optical transparency above 80% across the visible spectrum was obtained for sputtered ternary SnO2-TiO2 oxide films for oxygen partial pressure >19.4%. A positive correlation between optical bandgap and Ti/Sn ratio was observed. However, optical properties deteriorated as Ti-content increased in the as-deposited SnO2-TiO2-WO3 films. All studied as-deposited SnO2-TiO2-WO3 thin films were found to be highly resistive. X-ray diffraction data indicated no long-range structural order. %I Loughborough University