Wang, Dawei Zhang, Shiyu Zhou, Di Song, Kaixin Feteira, Antonio Vardaxoglou, J. C. Whittow, William Cadman, Darren Reaney, Ian M. Temperature stable cold sintered (Bi0.95Li0.05)(V0.9Mo0.1)O4-Na2Mo2O7 microwave dielectric composites Dense (Bi0.95Li0.05)(V0.9Mo0.1)O4-Na2Mo2O7 (100−x) wt.% (Bi0.95Li0.05)(V0.9Mo0.1)O4 (BLVMO)-x wt.% Na2Mo2O7 (NMO) composite ceramics were successfully fabricated through cold sintering at 150 °C under at 200 MPa for 30 min. X-ray diffraction, back-scattered scanning electron microscopy, and Raman spectroscopy not only corroborated the coexistence of BLVMO and NMO phases in all samples, but also the absence of parasitic phases and interdiffusion. With increasing NMO concentration, the relative pemittivity (εr) and the Temperature Coefficient of resonant Frequency (TCF) decreased, whereas the Microwave Quality Factor (Qf) increased. Near-zero TCF was measured for BLVMO-20wt.%NMO composites which exhibited εr ~ 40 and Qf ~ 4000 GHz. Finally, a dielectric Graded Radial INdex (GRIN) lens was simulated using the range of εr in the BLVMO-NMO system, which predicted a 70% aperture efficiency at 26 GHz, ideal for 5G applications. Cold sintering process;Microwave dielectric ceramics;Graded radial index lens;Mechanical Engineering not elsewhere classified 2019-04-30
    https://repository.lboro.ac.uk/articles/journal_contribution/Temperature_stable_cold_sintered_Bi0_95Li0_05_V0_9Mo0_1_O4-Na2Mo2O7_microwave_dielectric_composites/9572357