Microstructural and mechanical analysis on Cu-Sn intermetallic micro-joints under isothermal condition
2015-08-27T09:17:20Z (GMT) by
This study focuses on the mechanism of phase transformation from Cu6Sn5 into Cu3Sn and the homogenization process in full intermetallics (IMCs) micro-joints, which were prepared by soldering the initial Cu/Sn/Cu structure through high temperature storage in vacuum environment as the Transient Liquid Phase (TLP) process. From the microstructural observation by electron backscatter diffraction (EBSD), a mixture of IMCs phases (Cu6Sn5 and Cu3Sn) has been found to constitute the sandwich-structured Cu/IMCs/Cu joints. With the dwell time increasing at 533 K, there were two layers of Cu3Sn emerging from both sides of copper substrates with the depletion of Cu6Sn5 layer, toward merging each other in the IMCs interlayer. Then the Cu3Sn grains with various sizes became more homogenous columnar crystallites. Meanwhile, some equiaxial ultra-fine grains accompanied with the Kirkendall voids, were found only in adjacent to the electroplated copper. In addition, a specific type of micropillar with the size ∼5 μm × 5 μm × 12 μm fabricated by focus ion beam (FIB) was used to carry out the mechanical testing by Nano-indentation, which confirmed that this type of joint is mechanically robust, regardless of its porous Cu3Sn IMC interconnection.