Effects of electroplating on the mechanical properties of stereolithography and laser sintered parts

Download (74.49 kB)
journal contribution
posted on 31.07.2008 by Naguib Saleh, Neil Hopkinson, Richard J.M. Hague, Sean Wise
This paper provides a quantitative and qualitative assessment of the effects of electroplating on polymer parts made by stereolithography and laser sintering. A series of test samples were coated with copper and nickel with varying thickness. Thicker coatings (120μm) were reproduced with a repeatability that should not adversely affect the tolerances with which such parts may be produced given the tolerances of the initial rapid prototyping processes themselves. Thinner coatings (20μm) resulted in a smother surface finish than thicker coatings for stereolithography parts, however the converse was true for laser-sintered parts. Composite theory was used to predict that thicker coating would lead to higher Young’s modulus in parts and this was shown to be true in physical tests although the practical values were lower than the predicted values especially for thicker coatings. Physical tests also confirmed that thicker coatings increased UTS and impact energy but had a minimal effect on the ductility of parts.

History

School

  • Mechanical, Electrical and Manufacturing Engineering

Citation

SALEH, N. ... et al, 2004. Effects of electroplating on the mechanical properties of stereolithography and laser sintered parts. Rapid prototyping journal, 10 (5), pp. 305-315 [DOI: 10.1108/13552540410562340]

Publisher

© Emerald Group Publishing Limited

Publication date

2004

Notes

This is a journal article. It was published in the journal, Rapid prototyping journal [© Emerald] and the definitive version is available at: http://www.emeraldinsight.com/1355-2546.htm

ISSN

1355-2546

Language

en

Exports