Formation of twins in AlON material and its effects on the Vickers hardness and fracture toughness

Download (55.2 MB)
journal contribution
posted on 10.07.2019 by Maomao Ding, Tun Wang, Benjamin Maerz, Stuart Robertson, Zehan Sun, Lingcong Fan, Ying Shi, Houzheng Wu
Aluminum oxynitride (γ-AlON) powders were synchronously synthesized by carbothermal reduction-nitridation (CRN) and high-temperature solid state reaction (SSR) methods. Twin structures existing in γ-AlON powders and transparent AlON ceramics were investigated by systematically employing electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM). It was found that the twin structures in synthetic powder and transparent ceramics exhibit quite different microstructural features; binary twin structures were widely observed in powders and ceramics, whereas the sandwich-like twin structure was produced only in transparent ceramics. High-resolution electron backscattered diffraction (HREBSD) was used to determine the residual elastic stress distributions in AlON powders and ceramics. Discrepancies in the magnitude and distribution of the residual stress between binary twins and sandwich-like twins were fully clarified. The formation of two kinds of twins in powders and ceramics was discussed in detail. The Vickers hardness and its corresponding indentation size effect (ISE) were studied in CRN-AlON and SSR-AlON ceramics. The effects of the twin structure on the Vickers hardness and fracture toughness were investigated simultaneously.

Funding

National Natural Science Foundation of China (NO. 61475097).

History

School

  • Aeronautical, Automotive, Chemical and Materials Engineering

Department

  • Materials

Published in

Ceramics International

Volume

45

Issue

17, Part A

Pages

21127 - 21135

Citation

DING, M. ... et al, 2019. Formation of twins in AlON material and its effects on the Vickers hardness and fracture toughness. Ceramics International, 45 (17, Part A), pp.21127-21135.

Publisher

Elsevier

Version

AM (Accepted Manuscript)

Rights holder

© Elsevier Ltd and Techna Group S.r.l.

Publisher statement

This paper was accepted for publication in the journal Ceramics International and the definitive published version is available at https://doi.org/10.1016/j.ceramint.2019.07.089.

Acceptance date

08/07/2019

Publication date

2019-07-09

Copyright date

2019

ISSN

0272-8842

Language

en

Exports

Logo branding

Exports