Simulating radiation damage in Ga stabilised δ-Pu
journal contributionposted on 01.02.2013, 11:37 authored by Marc Robinson, Steven KennySteven Kenny, Roger SmithRoger Smith, M.T. Storr
Radiation events in Ga stablised δ-Pu are investigated by means of Molecular Dynamics simulations. Pu 5 at.% Ga is considered using the Modified Embedded Atom Method to govern the atomic interactions. Cascades were initiated with Primary Knock-on Atom (PKA) energies in the range of 0.4–10 keV, with trajectories deduced through comprehensive sampling of a representative set of directions, combined with different Ga atomic positions. The displacement threshold energy, Ed, for Pu and Ga atoms was also determined through similar extensive studies to aid the understanding and interpretation of the cascade results. Values of Ed between 5 and 40 eV were determined for Pu, with Ga PKAs requiring generally more energy to create a defect with Ed between 8 and 70 eV. Low energy collision cascades, initiated with energies in the range of 0.4–1 keV, show that the cascades form in a similar manner to other fcc metals with a vacancy rich zone surrounded by isolated interstitial defects. A feature of these cascades is that the displaced Ga atoms return to lattice sites during the ballistic phase, leading to a lack of Ga-type residual defects. Higher energy cascades show similar features but with the development of an amorphous region at the cascade core of around 5 nm diameter at 5 keV. Quantitatively, the residual number of defects found shows no distinct variation to that for previous work on pure Pu, suggesting the inclusion of Ga does not significantly effect the susceptibility or resistance of Pu to initial cascade development.
- Mathematical Sciences