A study of chain motions in some poly(ethers) by relaxation techniques: the influence of crystallinity and crystalline morphology

Download (3.55 MB)
thesis
posted on 08.11.2018, 17:00 by G.S. Fielding-Russell
The dynamic mechanical and dielectric properties of a number of morphologically different samples of poly(ethylene oxide) and poly(tetramethylene oxide) are reported over the temperature range -150°C to above the glass transition temperature. The dynamic mechanical measurements are by a vibrating reed technique at essentially constant frequency and the dielectric measurements are made over the range 10²–10⁶ Hz. Poly(ethylene oxide) exhibits two low temperature dielectric loss peaks: the higher temperature process (termed β-process) is ascribed to the glass-rubber transition of the amorphous phase; and the lower temperature process (termed α-process) is ascribed to a local mode oscillation of the chains. The polymer exhibits only one mechanical loss peak, a β-peak. [Continues.]

History

School

  • Science

Department

  • Chemistry

Publisher

© G.S. Fielding-Russell

Publisher statement

This work is made available according to the conditions of the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0) licence. Full details of this licence are available at: https://creativecommons.org/licenses/by-nc-nd/4.0/

Publication date

1967

Notes

A Doctoral Thesis. Submitted in partial fulfilment of the requirements for the award of the degree of Doctor of Philosophy at Loughborough University.

Language

en

Usage metrics

Keywords

Exports