Single step production of nanoporous electrospun poly(ε-caprolactone) fibres

Download (5.65 MB)
thesis
posted on 2016-10-24, 08:03 authored by Konstantinos A.G. Katsogiannis
Nanoporous polymer fibres are currently attracting increasing interest due to their unique characteristics. Increased specific surface area, improved mechanical properties and improved cellular growth are amongst the advantages that set porous fibres as ideal candidates in applications like catalysis, separation and tissue engineering. This work explores the single step production of porous poly(ε-caprolactone) (PCL) fibres through combinative electrospinning and Non-solvent Induced Phase Separation (NIPS) technique. Theoretical models, based on three different contact models (Hertzian, DMT, JKR), correlating the fibrous network specific surface area to material properties (density, surface tension, Young s modulus, Poisson s ratio) and network physical properties (density) and geometrical characteristics (fibre radius, fibre aspect ratio, network thickness) were developed in order to calculate the surface area increase caused by pore induction. Experimental results proved that a specific surface area increase of up to 56% could be achieved, compared to networks composed of smooth surfaced fibres. The good solvent effect on electrospun fibre surface morphology and size was examined through experimental investigation of four different good solvent (chloroform, dichloromethane, tetrahydrofuran and formic acid) based solutions at various good/poor solvent ratios. Chloroform was proven to be the most suitable solvent for good /poor solvent ratios varying from 75-90% v/v, whereas alternative mechanisms leading to different fibre morphologies were identified, interpreted and discussed. Evaporation rate of the good solvent was identified as the key parameter of the process. Second order polynomial equations, derived from the experimental data, correlating the feed solution physical parameters (viscosity, conductivity, surface tension) to the fibre average diameter produced were developed and validated. Response surface methodology was implemented for the design and conduction of electrospinning experiments on a 12.5 % w/v Chloroform/DMSO solution 90/10 % v/v in order to determine the individual process parameters (spinning distance, applied voltage, solution flow rate) effect in fibre surface morphology and size. The increase in any of these parameters results in increase of both the fibre size and the tendency for pore generation, whereas applied voltage was the parameter with the strongest effect. Findings from this thesis expand the knowledge about both phenomena occurring during the production process and end product properties, and can be used for the production of controlled morphology and size porous poly(ε-caprolactone) (PCL) fibres.

Funding

Graduate School of Loughborough University

History

School

  • Aeronautical, Automotive, Chemical and Materials Engineering

Department

  • Chemical Engineering

Publisher

© Konstantinos Alexandros Katsogiannis

Publisher statement

This work is made available according to the conditions of the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0) licence. Full details of this licence are available at: https://creativecommons.org/licenses/by-nc-nd/4.0/

Publication date

2016

Notes

A Doctoral Thesis. Submitted in partial fulfilment of the requirements for the award of Doctor of Philosophy of Loughborough University.

Language

  • en

Usage metrics

    Chemical Engineering Theses

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC